Lithium-conducting sulfur compound cathode for lithium-sulfur batteries

ABSTRACT

A lithium sulfur cell has a cathode including Li3PS4+n (0&lt;n&lt;9), an electrolyte, and an anode comprising lithium. A cathode for a lithium sulfur cell is also disclosed.

CROSS REFERENCE TO RELATED APPLICATIONS

This Application is a divisional application of U.S. application Ser. No. 13/974,854 filed Aug. 23, 2013, now U.S. Pat. No. 9,466,834, issued on Oct. 11, 2016, the entirety of which is hereby incorporated herein by reference.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH

This invention was made with government support under contract No. DE-AC05-00OR22725 awarded by the U.S. Department of Energy. The government has certain rights in this invention.

FIELD OF THE INVENTION

This invention relates generally to lithium-sulfur batteries, and more particularly to cathodes for lithium sulfur batteries.

BACKGROUND OF THE INVENTION

Global green-house and energy concerns have accelerated the electrification of vehicles, which has resulted in a great demand for rechargeable batteries with high energy and power densities. Among various rechargeable batteries for electric vehicles, lithium-ion (Li-ion) batteries have received much attention for their scientific and commercial significance. LiFePO₄, one of the most promising cathode materials in Li-ion batteries, has been widely studied owing to its low cost and environmental and safety characteristics. However, the practical application of LiFePO₄ was hindered for a long time due to its intrinsically low electronic and ionic conductivity. Good electronic and ionic conductivity are required from an electrode material for the long-term cycling of rechargeable lithium batteries. In response to the considerable challenges of LiFePO₄, many research groups proposed to improve its conductivities by reducing the particle size or coating particles with conductive materials such as carbon. The importance of good ionic and electronic conductivity from an electrode material has been proven by LiCoO₂, a cathode material widely used in Li-ion batteries which dominate the current electronics market. Therefore, although Li-ion batteries are considered to be a promising system for green transportation, reaching beyond their horizon is a formidable challenge due to the limited energy density which results from the low capacity of LiFePO₄ (170 mAh g⁻¹) and LiCoO₂ (136 mAh g−1). In comparison, the theoretically significantly higher capacity of sulfur (1,675 mAh g⁻¹) makes it emerge as one of the most promising cathode materials for rechargeable lithium batteries, i.e., lithium-sulfur (Li—S) batteries.

A typical Li—S cell includes sulfur as the positive electrode and lithium as the negative electrode, with a liquid electrolyte as both the charge transfer medium and ionic conductor within the sulfur-containing cathode. Under intense study for more than two decades, there is still no system that works well as a Li—S battery. This is due to the well-known fact that sulfur or sulfur compounds are not only highly electronically insulating but also ionically inactive. Until now, most research has been focused on the synthesis of carbon materials with high surface area for the electronic enhancement of the sulfur cathode. The liquid electrolyte has been used to improve the ionic conductivity of sulfur and its compounds that rely on dissolution in the liquid electrolyte. However, the dissolution of sulfur compounds lead to the polysulfide shuttle, which migrates sulfur species to chemically react with the lithium anode and results in the loss of active materials and poor cycling performance. Though many materials, such as nanostructured carbons, polymers, or graphene composites, were synthesized to retard the diffusion of the bulky polysulfides out of the cathode into electrolyte, the polysulfide shuttle cannot be fully prevented as evidenced by the gradual capacity fading during cycling. There remains a need to improve the intrinsic ionic conductivity of sulfur in Li—S batteries without depending on the liquid electrolyte.

SUMMARY OF THE INVENTION

A lithium sulfur cell includes a cathode comprising Li₃PS_(4+n) (0<n<9); an electrolyte; and an anode comprising lithium.

The cathode can comprise Li₃PS₅, Li₃PS₆, Li₃PS₇, Li₃PS₈, Li₃PS₉, Li₃PS₁₀, Li₃PS₁₁, Li₃PS₁₂, and combinations thereof.

The electrolyte can comprise lithium thiophosphate, lithium lanthanum zirconium oxide, lithium lanthanum titanium oxide, lithium boron hydride, and lithium iodide, and combinations thereof.

The anode can comprise at least one selected from the group consisting of lithium, silicon, silicon monoxide, tin, and tin oxide.

A cathode for a lithium sulfur cell comprises Li₃PS_(4+n) (0<n<9). The cathode can comprise Li₃PS₅, Li₃PS₆, Li₃PS₇, Li₃PS₈, Li₃PS₉, Li₃PS₁₀, Li₃PS₁₁, Li₃PS₁₂, and combinations thereof.

A method of making a cathode for a battery includes the step of reacting sulfur with Li₃PS₄ in a liquid solvent such as THF, acetonitrile, dimethoxylethane, glyme solvents and ethers to provide a composition comprising Li₃PS_(4+n) (0<n<9). A slurry is created with the compound, a binder and carbon. A cathode is then formed with the slurry.

BRIEF DESCRIPTION OF THE DRAWINGS

There are shown in the drawings embodiments that are presently preferred it being understood that the invention is not limited to the arrangements and instrumentalities shown, wherein:

FIG. 1 is a plot of the ionic conductivity of Li₃PS_(4+n) (n=5) in the temperature range of 20-80° C.

FIG. 2 is a plot of the ionic conductivity of Li₃PS_(4+n) (n=2, 3, 5, 6 and 8) at 25° C.

FIG. 3 is a plot of the cycling performance of Li₃PS_(4+n) (n=5) at the rate of C/10 at RT and 60° C.

FIG. 4 is a plot of the voltage profile of Li₃PS_(4+n) (n=5) at room temperature.

FIG. 5 is a plot of the voltage profile of Li₃PS_(4+n) (n=5) at 60° C.

FIG. 6 is a plot of the rate capabilities of Li₃PS_(4+n) (n=5) from C/10-2C at 60° C.

FIG. 7 is an XRD pattern of S, Li₃PS₄ and Li₃PS_(4+n) (n=5) at room temperature and 80° C.

FIG. 8 is a plot of the Raman spectra of S, Li₃PS₄ and Li₃PS_(4+n) (n=3, 5 and 6).

FIG. 9 is a plot of the Raman shift between the wavelengths of 125-175 cm⁻¹.

FIG. 10 is a plot of the Raman's shift between the wavelengths of 460-490 cm⁻¹.

FIG. 11 is a plot of the coulombic efficiency of Li₃PS_(4+n) (n=5) at room temperature and 60° C.

FIG. 12 is a scanning electron microscope (SEM) image of Li₃PS_(4+n) (n=5) before cycling at 60° C.

FIG. 13 is a scanning electron microscope (SEM) image of Li₃PS_(4+n) (n=5) after cycling at 60° C.

FIG. 14 is a schematic diagram of a lithium-sulfur cell according to the invention.

DETAILED DESCRIPTION OF THE INVENTION

A lithium sulfur cell includes a cathode comprising Li₃PS_(4+n) (0<n<9), an electrolyte; and an anode comprising lithium. The cathode can comprise at least one of Li₃PS₅, Li₃PS₆, Li₃PS₇, Li₃PS₈, Li₃PS₉, Li₃PS₁₀, Li₃PS₁₁, Li₃PS₁₂, and mixtures thereof.

The electrolyte can be any suitable electrolyte. The electrolyte can comprise lithium thiophosphate, lithium lanthanum zirconium oxide, lithium lanthanum titanium oxide, lithium boron hydride, and lithium iodide, and any combination of these compounds.

Any suitable anode construction can be utilized, including, for example and without limitation, lithium, silicon, silicon monoxide, tin, and tin oxide.

A lithium-conducting sulfur compound according to the invention has an ionic conductivity of 3.0×10⁻⁵ S cm⁻¹ at 25° C. (FIG. 1), which is 5 orders of magnitude higher than that of Li₂S (2×10⁻¹⁰ S cm⁻¹) of prior lithium sulfur cells. This ionic conductivity is comparable to that of LiFePO₄ (5.0×10⁻⁵ S cm⁻¹) and LiCoO₂ (7.2×10⁻⁵ S cm⁻¹).

The sulfur compound of the invention shows near-theoretical capacity, which is 10 times higher than LiFePO₄ and long-term cyclability of 300 cycles without significant capacity decay due to the elimination of the polysulfide shuttle. With increase in temperature, the ionic conductivity of this sulfur compound Li₃PS_(4+n) (n=5) improves by one order of magnitude, from 10⁻⁵ S cm⁻¹ at 25° C. to 10⁻⁴ S cm⁻¹ at 60° C. The activation energy is 0.37 eV. Moreover, with an increase in the sulfur content within the compound, the ionic conductivity of the compound Li₃PS_(4+n) decreases (FIG. 2). However, the ionic conductivity of the sulfur compound Li₃PS_(4+n), for example at n=8, is still within the range of 10⁻⁵ S cm⁻¹ at 25° C.

The sulfur compound Li₃PS_(4+n) (0<n<9) of the invention can be synthesized by any suitable reaction methodology. In one aspect, the sulfur compound of the invention is synthesized through the wet-chemical reaction of the solid electrolyte Li₃PS₄ and elemental sulfur in tetrahydrofuran (THF). Sulfur is reacted with Li₃PS₄ in a liquid solvent such as THF, acetonitrile, dimethoxylethane, glyme solvents and ethers to produce Li₃PS_(4+n). The reaction in one embodiment is conducted at room temperature but can be conducted at any temperature in the liquid temperature range of the solvent. The reaction is insensitive to concentration and pressure.

The compound Li₃PS_(4+n) (n=5) used as the cathode material in rechargeable lithium batteries at room temperature (RT) shows an initial discharge capacity of 1,272 mAh g⁻¹ (based on the sulfur content) or 599 mAh g⁻¹ (based on the sulfur compound) with a reversibility of 95% (FIG. 3). After a few cycles, the reversibility gradually increases to 100% (FIG. 11). Such a high coulombic efficiency indicates the elimination of the polysulfide shuttle, which has been proven to be the main cause of low coulombic efficiency in Li—S battery cells when using the liquid electrolyte. After 300 cycles the capacity is stable at 700 mAh g⁻¹. The capacities are normalized to the sulfur content in the compound; however, the normalized capacities based on the compound are also shown. The good reversibility and excellent cycling performance is due to the great improvement in the ionic conductivity of this sulfur compound without relying on the liquid electrolyte and subsequently the elimination of polysulfide shuttle.

In order to further confirm the importance of the ionic conductivity, a Li—S cell was tested using Li₃PS_(4+n) (n=5) as the cathode material at 60° C., since its ionic conductivity is one order of magnitude improved from 10⁻⁵ S cm⁻¹ at 25° C. to 10⁻⁴ S cm⁻¹ at 60° C. (FIG. 1). Compared to the voltage profile at RT, the charge/discharge potential difference of the sulfur compound is greatly reduced; while the energy efficiency of the cathode electrode is enhanced from 59.7% at RT to 82.8% at 60° C. (FIGS. 4 and 5). Unlike two plateaus in the voltage profile when using liquid electrolytes, there is just one plateau when using this sulfur compound as the cathode material in Li—S batteries. In FIG. 3, the initial discharge capacity of the sulfur compound is 1,401 mAh g⁻¹, which accounts for the 83.6% of sulfur utilization based on the theoretical maximum 1,675 mAh g⁻¹. Slight capacity fading is observed before the 50^(th) cycle, and then the discharge capacity stabilizes at 1,200 mAh g⁻¹. After 300 cycles, the discharge capacity of the sulfur compound still remains above 1,000 mAh g⁻¹. The experimental cell has a high initial coulombic efficiency of 98.5% and a coulombic efficiency of 100% after 50 cycles (FIG. 11). The excellent cycling performance is due to the good ionic conductivity of the sulfur compound and complete electrode integrity without using the liquid electrolyte, as shown in FIGS. 12-13.

Due to the one magnitude enhancement of the ionic conductivity of the sulfur compound Li₃PS_(4+n) (n=5) from RT to 60° C., the sulfur compound as the cathode material in Li—S batteries under was tested at high current densities at 60° C., and the results are shown in FIG. 6. While the current density increases from C/10 to 2C, the capacity of the sulfur compound decreases slightly. The cell shows a reversible capacity of 735 mAh g⁻¹ at 2C after 50 cycles at various rates, and further cycling at a low rate of C/10 brings it back to a reversible capacity of 1,200 mAh g⁻¹. FIG. 6 demonstrates the benefit of having a sulfur compound with superionic conductivity for high power density lithium batteries, because the excellent ionic conductivity of the sulfur compound greatly improves the electrode kinetics at the elevated temperature of 60° C.

A series of sulfur compounds Li₃PS_(4+n) (0<n<9) were synthesized. The weak chemical bonds between sulfur and Li₃PS₄ in the sulfur compounds make them dissolve well in THF, compared to the solubility of sulfur and Li₃PS₄. Equation 1 illustrates the reaction between sulfur and Li₃PS₄

At the beginning, free radicals are determined by the following rapid radical displacement reaction, as shown in equation 2: —S′_(i) ⁻+—S—S—

—S_(i)—S′⁻+—S— The activation energy for the above reaction is derived as 12 kJ mol⁻¹. The radicals are believed to move rapidly around and chain-like molecules are constantly formed. With more sulfur adding to the solution, the average length (n) of the sulfur chain increases, and the colors of the solution become darker. When these sulfur compounds are used as cathode materials in rechargeable lithium batteries, it is feasible to have the disulfide (—S—S—) redox couple cycled via a highly reversible redox reaction. Organosulfur compounds with the thiol (—SH)/disulfide (—S—S—) redox couple have been reported as cathode materials in rechargeable lithium batteries; however, they have poor ionic conductivity and low capacity. In comparison, the sulfur compound Li₃PS_(4+n) (0<n<9) can store large amounts of charge per unit mass in rechargeable lithium batteries, even up to 1,000 mAh g⁻¹ (based on the compound) with the increase in the sulfur content; however, the ionic conductivity of the compound decreases (FIG. 2). Thus in order to enhance the lithium storage capacity of the compound, the sulfur loading can be high but the cycling current density could be sacrificed.

Equation 3 illustrates the mechanism during charge/discharge.

X-ray diffraction (XRD) and Raman spectra in FIG. 3 verify the chemical structure of the sulfur compound. Compared to the sulfur and Li₃PS₄ in FIG. 7, a new crystalline structure of the sulfur compound Li₃PS_(4+n) (n=5) is formed during synthesis. After the removal of the THF at 80° C. under vacuum, the Li₃PS₄ become amorphous while the Li₃PS_(4+n) (n=5) is still in the crystalline form. The crystalline structure of the sulfur compound becomes different compared to that at RT. From the Raman spectra in FIG. 8, the predominate peak of the Li₃PS_(4+n) (n=3, 5, and 6) at 418 cm⁻¹ is due to the symmetric stretching of the —P—S bond and the weak peak of 184 cm⁻¹ is from the stretching vibrations of the —P—S bond in PS₄ ³⁻ ions with T_(d) symmetry; the peaks centered at 155 cm⁻¹, 218/476 cm⁻¹, and 248/437 cm⁻¹ are assigned to the E₂, A₁, and E₃ symmetry species of the —S—S— bond, respectively. With decrease in the sulfur content in the compound, the —S—S— bond peaks at 155 and 476 cm⁻¹ shift to the lower wavelength (FIGS. 9 and 10), which result from the vibration effect of the P—S bond in PS₄ ³⁻ and the length of sulfur chain in the compound.

EXAMPLE

The sulfur compound Li₃PS_(4+n) (n=2, 3, 5, 6, and 8) was synthesized through the wet-chemical reaction of the solid electrolyte Li₃PS₄ and elemental sulfur in the solvent of tetrahydrofuran (THF) under sonication. After being fully dissolved, the sulfur compound was heat-treated under vacuum for 2 hours at 80° C. to remove the THF. A cathode slurry was prepared with the sulfur compound (60 wt %), WVA-1500 carbon (MeadWestvaco Corporation, 30 wt %), and PVC binder (10 wt %) using THF as the solvent. After 0.5 hour's sonication, the cathode slurry was coated on the solid electrolyte side of the pilot, which was pressed by the lithium metal and solid electrolyte Li₃PS₄ under 8 MPa. The diameter and the thickness of the pilot were 0.5 inch (1.27 cm) and 0.5 mm, respectively. The pilot of the sulfur compound was also prepared under 8 MPa for its conductivity measurement.

The ionic conductivity of the sulfur compound was determined in the frequency range of 10 MHz to 1 Hz with an amplitude of 10 mV by using a frequency response analyzer (Solartron 1260). Swagelok cells were used to evaluate the cycling performance. Low surface area carbon black (surface area ˜50 m²/g) coated aluminum foil was used as the current collector. Charge and discharge were carried out using a Maccor 4000 series battery tester at a current density of 0.015 mA cm⁻² (C/10) between the cut-off potentials of 1.5-2.8 V vs. Li/Li⁺. The current densities of 0.03 (C/5), 0.075 (C/2.5), 0.15 (C), and 0.2 (2C) mA cm⁻² were applied to measure the rate capabilities of the sulfur compound cathode. The calculation of specific charge/discharge capacities was based on the mass of sulfur and the compound, respectively.

The structures of the cathode electrode before and after cycling were examined using a field emission STEM (Hitachi HF-3300) at 15 kV. The elemental mapping of the samples was also taken using STEM. X-ray diffraction (XRD) analysis was performed at a PANalytical X'pert PRO2-circle X-ray diffractometer with a CuKα radiation (λ=1.5418 Å). Raman spectroscopy was recorded from 600 to 100 cm⁻¹ on a Renishaw Confocal MicroRaman spectrometer at room temperature.

A cell according to the invention can have any suitable construction. A lithium-sulfur cell comprising Li₃PS_(4+n) (0<n<9) is shown in FIG. 14. The cell can include, for example, current collector 20, anode 24, electrolyte 28, cathode 32, and current collector 36. The cathode 32 includes Li₃PS_(4+n) (0<n<9).

The sulfur compound of the invention has a superionic conductivity of 2.5×10⁻⁵ S cm⁻¹ at 25° C., and is a good cathode material with a high initial discharge capacity of 1,300 mAh g⁻¹, almost 100% coulombic efficiency, and about 60% capacity retention after 300 cycles at RT. The excellent cycling performance is due to the enhancement of the ionic conductivity of the sulfur compound without depending on the liquid electrolyte and subsequently the elimination of polysulfide shuttle. The importance of the ionic conductivity is confirmed by the improved cycling performance, energy efficiency, and rate capabilities at 60° C. due to the enhancement of the ionic conductivity by one order of magnitude to 1.0×10⁻⁴ S cm⁻¹.

Although this sulfur compound was tested in solid state lithium batteries, it could be used as an electrolyte for sensors, solar cells, and supercapacitors. A wide variety of compounds with good ionic conductivity could be synthesized and find broad applications in many areas of materials science, in addition to the electrode materials for high energy density rechargeable lithium batteries.

This invention can be embodied in other forms without departing from the spirit of the invention, and therefore reference should be had to the following claims as indicating the scope of the invention: 

We claim:
 1. A method of making a cathode for a battery, comprising the steps of: reacting sulfur with Li₃PS₄ in a liquid solvent to provide a composition comprising Li₃PS_(4+n) (0<n<9), where n is an integer; creating a slurry with the compound, a binder and carbon; and coating a current collector with the slurry and forming a cathode with the slurry.
 2. The method of claim 1, wherein the solvent is at least one selected from the group consisting of tetrahydrofuran, acetonitrile, dimethoxylethane, glyme solvents and ethers.
 3. The method of claim 1, wherein Li₃PS_(4+n) comprises Li₃PS₅.
 4. The method of claim 1, wherein Li₃PS_(4+n) comprises Li₃PS₆.
 5. The method of claim 1, wherein Li₃PS_(4+n) comprises Li₃PS₇.
 6. The method of claim 1, wherein Li₃PS_(4+n) comprises Li₃PS₈.
 7. The cathode of claim 1, wherein Li₃PS_(4+n) comprises Li₃PS₉.
 8. The method of claim 1, wherein Li₃PS_(4+n) comprises Li₃PS₁₀.
 9. The method of claim 1, wherein Li₃PS_(4+n) comprises Li₃PS₁₁.
 10. The method of claim 1, wherein Li₃PS_(4+n) comprises Li₃PS₁₂.
 11. A method of making a battery, comprising the steps of: preparing a cathode, comprising the steps of reacting sulfur with Li₃PS₄ in a liquid solvent to provide a composition comprising Li₃PS_(4+n) (0<n<9), where n is an integer; creating a cathode slurry with the composition, a binder and carbon; coating a current collector with the slurry to form a cathode; and combining the cathode with an electrolyte and an anode to form a battery.
 12. The method of claim 11, wherein the solvent is at least one selected from the group consisting of tetrahydrofuran, acetonitrile, dimethoxylethane, glyme solvents and ethers.
 13. The method of claim 11 wherein the anode comprises at least one selected from the group consisting of lithium, silicon, silicon monoxide, tin, and tin oxide.
 14. The method of claim 11, wherein Li₃PS_(4+n) comprises Li₃PS₅.
 15. The method of claim 11, wherein Li₃PS_(4+n) comprises Li₃PS₆.
 16. The method of claim 11, wherein Li₃PS_(4+n) comprises Li₃PS₇.
 17. The method of claim 11, wherein Li₃PS_(4+n) comprises Li₃PS₈.
 18. The cathode of claim 11, wherein Li₃PS_(4+n) comprises Li₃PS₉.
 19. The method of claim 11, wherein Li₃PS_(4+n) comprises Li₃PS₁₀.
 20. The method of claim 11, wherein Li₃PS_(4+n) comprises Li₃PS₁₁.
 21. The method of claim 11, wherein Li₃PS_(4+n) comprises Li₃PS₁₂. 